it is, in fact, I had tried cos? , taking my place on the ferrule of the staganvo and when I went to ****llo of the hole and then melt the tin to make it weld to the hole but nada....I attacked....even if the e xxx bdm of the cock as you saw in the photos I have found difficulty? of this kind, even if the result is not ? was excellent...but I have reached the goal....
Guys I would like information such as names and what should I ask in an electronics shop to have the strips that are welded to the bdm? I have a edc16 to be evidence of welding....
thanks
Strip 2,54mmOriginally Written by ducati83
Yep, still not happy with my solder . The first when I use solder paste and with the stagnantore balance join me for the Pin, the dough is placed on the eprom on the card, let's say just where it ends in the Eprom?
Can I use the pasta welded and dissolve it in hot air? Or risk getting to merge the Pin
the last thing the temperature to use the stagnantore which should it be? Why? I do not melts the pond, I just got it I do not understand.
watch I am also a novice....then I flux I have no problems if I use the hot air....but with the style, sincerely, I have not seen the usefulness? of this product due to my lack of experience....even if the net I've seen many videos where is applied the flux, then put the eeprom and with the stylus and the tin wire to do a direct solder in the sequence, all the pins....so what you said can you? do with hot air station...everything ? understand how to ..or better have the right maestranza...
are also called connectors, tulip-shaped , for the bosch edc16 step ? 2.54 mm as it says overspeed !
if you join any of the pins you have used too much pond , or you did not clean well . The tip of the soldering iron should be cleaned compulsorily by the oxides ... the solder paste I don't use it , you can also be welded with hot air, and the pins do not join if you will be well-cleaned them, and the plots, clearly ? the quantity? of pasta, which must be moderate.... the other thing that I've seen over the years ? the stations are welded to the economic are not as reliable as temperature reading, etc, and then the council primary ? to do the tests rather than to rely on a number that does not correspond to reality?..
Last edited by leandro89; 17-02-2014 to 22:03
Once unsoldered hot air, the pitches must be removed from the pond? or is it enough to give a small smoothed with canvas brasiva?
how to weld hot air without solder paste? untie the pond..
you from the pitches remove the pond in excess , then make a pass with the flux for a uniform and disossidare all.
the abrasive cloth of the leave at the hardware store... I've never used it.
exact station, smd, you can dissolve the pond, the flux that ? on the plate I to do? the rest of it.
so if I understood well the pond is enough already that c'? in pizzola after I unsoldered, not I have to put even when the balance with the air.
sorry, but I'm doing several tests and I would like to make good welds.
if the pitches are tinned and disossidate , not to serve? add another then clearly depends on what we're talking about plcc , psop , soic , dil........... each has its own needs
Write permission
Quote